• LNP STAT-LOY PC 63000TXB
LNP™ STAT-LOY™ Compound PC 63000TXB
Also known as:LNP™ Stat-loy™ Compound 63000TXB Product reorder name:63000TXB
LNP* Stat-Loy* 63000TXB is a product based on Polycarbonate/Polyester resin featuring a permanent anti-static characteristic. Added features include: Transparent, Formulated with FDA Food Contact Additives and Bioassessed to ISO 10993.
Property
TYPICAL PROPERTIES(1)
MECHANICAL Value Unit Standard
Tensile Stress,brk,Type I,5mm/min 360 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5mm/min 5 % ASTM D 638
Tensile Modulus,5mm/min 12800 kgf/cm² ASTM D 638
Flexural Stress,brk,1.3mm/min,50mm span 500 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 12400 kgf/cm² ASTM D 790
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 147 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 85 cm-kgf/cm ASTM D 256
THERMAL Value Unit Standard
HDT,1.82 MPa,3.2mm,unannealed 71 ℃ ASTM D 648
PHYSICAL Value Unit Standard
Specific Gravity 1.15 - ASTM D 792
ELECTRICAL Value Unit Standard
Volume Resistivity 1.E+10-1.E+12 Ohm-cm ASTM D 257
Surface Resistivity 1.E+10-1.E+12 Ohm ASTM D 257
Static Decay,5000V to <50V <2 < seconds FTMS101B
Source GMD,last updated:2011/06/27
Parameter Injection Molding Value Unit
Drying Temperature 70-80 ℃
Drying Time 4 hrs
Maximum Moisture Content 0.05-0.1 %
Melt Temperature 200-210 ℃
Front-Zone 3 Temperature 205-215 ℃
Middle-Zone 2 Temperature 195-205 ℃
Rear-Zone 1 Temperature 180-195 ℃
Mold Temperature 10-50 ℃
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm